ASTM A276/A276M S32760 vs EN 10088-1 X2CrNiMoCuWN25-7-4

Strong Match — 98.7% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32760 (ASTM A276/A276M:2017) and EN 10088-1 X2CrNiMoCuWN25-7-4 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32760 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrNiMoCuWN25-7-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S32760 vs EN 10088-1 X2CrNiMoCuWN25-7-4 is a 98.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.7%.

Frequently Compared With ASTM A276/A276M S32760:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
98.7%
MECHANICAL MATCH
No shared data
OVERALL
98.7%
Specifications
Property ASTM A276/A276M S32760 EN 10088-1 X2CrNiMoCuWN25-7-4
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.030 <=0.035
S (%) <=0.010 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 24.0-26.0 24.0-26.0
Ni (%) 6.0-8.0 6.0-8.0
Mo (%) 3.0-4.0 3.0-4.0
N (%) 0.20-0.30 0.20-0.30
Cu (%) 0.50-1.00 0.50-1.00
W (%) 0.50-1.00 0.50-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32760 EN 10088-1 X2CrNiMoCuWN25-7-4
Tensile Strength >=750 MPa Not specified
Yield Strength >=550 MPa Not specified
Elongation >=25% Not specified
Hardness <=310 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S32760
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X2CrNiMoCuWN25-7-4
Not documented
Can ASTM A276/A276M S32760 Be Substituted With EN 10088-1 X2CrNiMoCuWN25-7-4?
ASTM A276/A276M S32760 and EN 10088-1 X2CrNiMoCuWN25-7-4 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoCuWN25-7-4 is often considered as a substitute for ASTM A276/A276M S32760 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S32760
0 active listings and RFQs →
EN 10088-1 X2CrNiMoCuWN25-7-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32760 and EN 10088-1 X2CrNiMoCuWN25-7-4?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S32760 be substituted with EN 10088-1 X2CrNiMoCuWN25-7-4?
ASTM A276/A276M S32760 and EN 10088-1 X2CrNiMoCuWN25-7-4 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoCuWN25-7-4 is often considered as a substitute for ASTM A276/A276M S32760 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.