ASTM A276/A276M S34565 vs ASTM A959 S34565

Strong Match — 97.2% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S34565 (ASTM A276/A276M:2017) and ASTM A959 S34565 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S34565 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 S34565 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S34565 is defined under ASTM International, originating from United States, while ASTM A959 S34565 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S34565 vs ASTM A959 S34565 is a 97.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 97.2%.

Frequently Compared With ASTM A276/A276M S34565:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
97.2%
MECHANICAL MATCH
No shared data
OVERALL
97.2%
Specifications
Property ASTM A276/A276M S34565 ASTM A959 S34565
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) 5.0-7.0 5.0-7.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.010
Si (%) <=1.00 <=1.00
Cr (%) 23.0-25.0 23.0-25.0
Ni (%) 16.0-18.0 16.0-18.0
Mo (%) 4.0-5.0 4.0-5.0
N (%) 0.40-0.60 0.40-0.60
Nb (%) <=0.10 Not specified
Cb (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S34565 ASTM A959 S34565
Tensile Strength >=795 MPa Not specified
Yield Strength >=415 MPa Not specified
Elongation >=35% Not specified
Typical Applications
ASTM A276/A276M S34565
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 S34565
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A276/A276M S34565 Be Substituted With ASTM A959 S34565?
ASTM A276/A276M S34565 and ASTM A959 S34565 overlap closely enough on chemistry and mechanical properties that ASTM A959 S34565 is often considered as a substitute for ASTM A276/A276M S34565 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S34565
0 active listings and RFQs →
ASTM A959 S34565
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S34565 and ASTM A959 S34565?
ASTM A276/A276M S34565 specifies Nb which is not specified for ASTM A959 S34565. ASTM A959 S34565 specifies Cb which is not specified for ASTM A276/A276M S34565.
Can ASTM A276/A276M S34565 be substituted with ASTM A959 S34565?
ASTM A276/A276M S34565 and ASTM A959 S34565 overlap closely enough on chemistry and mechanical properties that ASTM A959 S34565 is often considered as a substitute for ASTM A276/A276M S34565 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.