ASTM A276/A276M S34565 vs EN 10088-1 X2CrNiMnMoN25-18-6-5

Strong Match — 87% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S34565 (ASTM A276/A276M:2017) and EN 10088-1 X2CrNiMnMoN25-18-6-5 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S34565 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S34565 vs EN 10088-1 X2CrNiMnMoN25-18-6-5 is a 87% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87%.

Frequently Compared With ASTM A276/A276M S34565:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
87%
MECHANICAL MATCH
No shared data
OVERALL
87%
Specifications
Property ASTM A276/A276M S34565 EN 10088-1 X2CrNiMnMoN25-18-6-5
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) 5.0-7.0 5.0-7.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 23.0-25.0 24.0-26.0
Ni (%) 16.0-18.0 16.0-19.0
Mo (%) 4.0-5.0 4.0-5.0
N (%) 0.40-0.60 0.30-0.60
Nb (%) <=0.10 <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S34565 EN 10088-1 X2CrNiMnMoN25-18-6-5
Tensile Strength >=795 MPa Not specified
Yield Strength >=415 MPa Not specified
Elongation >=35% Not specified
Typical Applications
ASTM A276/A276M S34565
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X2CrNiMnMoN25-18-6-5
Not documented
Can ASTM A276/A276M S34565 Be Substituted With EN 10088-1 X2CrNiMnMoN25-18-6-5?
ASTM A276/A276M S34565 and EN 10088-1 X2CrNiMnMoN25-18-6-5 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMnMoN25-18-6-5 is often considered as a substitute for ASTM A276/A276M S34565 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S34565
0 active listings and RFQs →
EN 10088-1 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S34565 and EN 10088-1 X2CrNiMnMoN25-18-6-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S34565 be substituted with EN 10088-1 X2CrNiMnMoN25-18-6-5?
ASTM A276/A276M S34565 and EN 10088-1 X2CrNiMnMoN25-18-6-5 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMnMoN25-18-6-5 is often considered as a substitute for ASTM A276/A276M S34565 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.