ASTM A276/A276M S34800 vs IS 1570 (Part 5) X04Cr18Ni10Ti

Strong Match — 93.7% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S34800 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X04Cr18Ni10Ti (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S34800 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S34800 vs IS 1570 (Part 5) X04Cr18Ni10Ti is a 90.5% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 93.7%.

Frequently Compared With ASTM A276/A276M S34800:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4845 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
90.5%
MECHANICAL MATCH
100%
OVERALL
93.7%
Specifications
Property ASTM A276/A276M S34800 IS 1570 (Part 5) X04Cr18Ni10Ti
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 17.0-19.0 17.0-19.0
Ni (%) 9.0-12.0 9.0-12.0
Ta (%) <=0.10 Not specified
Co (%) <=0.20 Not specified
Nb (%) <=1.10 Not specified
Ti (%) Not specified >=5xC, <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S34800 IS 1570 (Part 5) X04Cr18Ni10Ti
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=205 MPa (0.2 % proof stress)
Elongation >=40% >=40% (50 mm)
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=183 HB; <=88 HRB
Typical Applications
ASTM A276/A276M S34800
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X04Cr18Ni10Ti
Not documented
Key Differences
Can ASTM A276/A276M S34800 Be Substituted With IS 1570 (Part 5) X04Cr18Ni10Ti?
ASTM A276/A276M S34800 and IS 1570 (Part 5) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr18Ni10Ti is often considered as a substitute for ASTM A276/A276M S34800 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S34800
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr18Ni10Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S34800 and IS 1570 (Part 5) X04Cr18Ni10Ti?
ASTM A276/A276M S34800 specifies Ta, Co, Nb which are not specified for IS 1570 (Part 5) X04Cr18Ni10Ti. IS 1570 (Part 5) X04Cr18Ni10Ti specifies Ti which is not specified for ASTM A276/A276M S34800.
Can ASTM A276/A276M S34800 be substituted with IS 1570 (Part 5) X04Cr18Ni10Ti?
ASTM A276/A276M S34800 and IS 1570 (Part 5) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr18Ni10Ti is often considered as a substitute for ASTM A276/A276M S34800 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.