ASTM A276/A276M S41040 vs EN 10088-1 X6Cr13

Close Alternative — 82.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S41040 (ASTM A276/A276M:2017) and EN 10088-1 X6Cr13 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S41040 is defined under ASTM International, originating from United States, while EN 10088-1 X6Cr13 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S41040 vs EN 10088-1 X6Cr13 is a 82.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.9%.

Frequently Compared With ASTM A276/A276M S41040:
IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
82.9%
MECHANICAL MATCH
No shared data
OVERALL
82.9%
Specifications
Property ASTM A276/A276M S41040 EN 10088-1 X6Cr13
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.18 <=0.08
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 11.0-13.0 12.0-14.0
Nb (%) 0.05-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S41040 EN 10088-1 X6Cr13
Tensile Strength >=480 MPa Not specified
Yield Strength >=275 MPa Not specified
Elongation >=13% Not specified
Hardness <=235 HB Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S41040
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X6Cr13
Not documented
Key Differences
Can ASTM A276/A276M S41040 Be Substituted With EN 10088-1 X6Cr13?
ASTM A276/A276M S41040 and EN 10088-1 X6Cr13 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M S41040
0 active listings and RFQs →
EN 10088-1 X6Cr13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S41040 and EN 10088-1 X6Cr13?
ASTM A276/A276M S41040 specifies Nb which is not specified for EN 10088-1 X6Cr13.
Can ASTM A276/A276M S41040 be substituted with EN 10088-1 X6Cr13?
ASTM A276/A276M S41040 and EN 10088-1 X6Cr13 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.