ASTM A276/A276M S41400 vs ASTM A959 414

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S41400 (ASTM A276/A276M:2017) and ASTM A959 414 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S41400 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 414 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S41400 is defined under ASTM International, originating from United States, while ASTM A959 414 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S41400 vs ASTM A959 414 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A276/A276M S41400:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A276/A276M S41400 ASTM A959 414
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.15
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 11.5-13.5 11.5-13.5
Ni (%) 1.25-2.50 1.25-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S41400 ASTM A959 414
Hardness <=298 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S41400
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 414
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M S41400 Be Substituted With ASTM A959 414?
ASTM A276/A276M S41400 and ASTM A959 414 overlap closely enough on chemistry and mechanical properties that ASTM A959 414 is often considered as a substitute for ASTM A276/A276M S41400 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S41400
0 active listings and RFQs →
ASTM A959 414
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S41400 and ASTM A959 414?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S41400 be substituted with ASTM A959 414?
ASTM A276/A276M S41400 and ASTM A959 414 overlap closely enough on chemistry and mechanical properties that ASTM A959 414 is often considered as a substitute for ASTM A276/A276M S41400 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.