Minimal Match — 34.9% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S41425 (ASTM A276/A276M:2017) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S41425 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
ASTM A276/A276M S41425 is defined under ASTM International, originating from United States, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, ASTM A276/A276M S41425 vs EN 10088-1 1.4845 is a 52.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 34.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S41425
EN 10088-1 1.4845
Tensile Strength
>=825 MPa
≥515 MPa
Yield Strength
>=655 MPa
≥205 MPa
Elongation
>=15%
≥40%
Hardness
<=321 HB
Not specified
Condition
Condition T (Hardened and tempered, higher temperature), hot-finished, all sizes (first row printed)
Not specified
Max Service Temp
Not specified
1100°C continuous
Typical Applications
ASTM A276/A276M S41425
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
ASTM A276/A276M S41425 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4845.
Can ASTM A276/A276M S41425 Be Substituted With EN 10088-1 1.4845?
ASTM A276/A276M S41425 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A276/A276M S41425 and EN 10088-1 1.4845?
ASTM A276/A276M S41425 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4845.
Can ASTM A276/A276M S41425 be substituted with EN 10088-1 1.4845?
ASTM A276/A276M S41425 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.