ASTM A276/A276M S41500 vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S41500 (ASTM A276/A276M:2017) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S41500 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. ASTM A276/A276M S41500 is defined under ASTM International (United States).

As per chemical composition, ASTM A276/A276M S41500 vs GOST 5632 06Kh23N28 is a 62.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S41500:
ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 25-4-4 GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
62.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A276/A276M S41500 GOST 5632 06Kh23N28
Standard ASTM A276/A276M:2017 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.05 ≤0.06
Mn (%) 0.50-1.00 ≤2.00
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Si (%) <=0.60 ≤0.80
Cr (%) 11.5-14.0 22.0–25.0
Ni (%) 3.5-5.5 26.0–29.0
Mo (%) 0.50-1.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S41500 GOST 5632 06Kh23N28
Tensile Strength >=795 MPa ≥510 MPa
Yield Strength >=620 MPa ≥196 MPa
Elongation >=15% ≥35%
Hardness <=295 HB Not specified
Condition Condition T (Hardened and tempered, higher temperature), hot-finished or cold-finished, all sizes (first row printed) Not specified
Max Service Temp Not specified 1050°C
Typical Applications
ASTM A276/A276M S41500
Stainless steel bars and shapes (hot-finished or cold-finished)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can ASTM A276/A276M S41500 Be Substituted With GOST 5632 06Kh23N28?
ASTM A276/A276M S41500 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S41500
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
ASTM A276/A276M S41500
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S41500 and GOST 5632 06Kh23N28?
ASTM A276/A276M S41500 specifies P, S, Mo which are not specified for GOST 5632 06Kh23N28.
Can ASTM A276/A276M S41500 be substituted with GOST 5632 06Kh23N28?
ASTM A276/A276M S41500 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.