ASTM A276/A276M S42010 vs IS 1570 (Part 7) 12Cr12MoVH

Related Material — 68.2% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S42010 (ASTM A276/A276M:2017) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S42010 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. ASTM A276/A276M S42010 is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S42010 vs IS 1570 (Part 7) 12Cr12MoVH is a 68.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 68.2%.

Frequently Compared With ASTM A276/A276M S42010:
GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
68.2%
MECHANICAL MATCH
No shared data
OVERALL
68.2%
Specifications
Property ASTM A276/A276M S42010 IS 1570 (Part 7) 12Cr12MoVH
Standard ASTM A276/A276M:2017 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.15-0.30 0.08-0.16
Mn (%) <=1.00 0.40-1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.035
Si (%) <=1.00 <=0.60
Cr (%) 13.5-15.0 11.5-13.00
Ni (%) 0.35-0.85 <=1.0
Mo (%) 0.40-0.85 0.40-0.80
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S42010 IS 1570 (Part 7) 12Cr12MoVH
Hardness <=235 HB Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Tensile Strength Not specified 770-930 MPa
Yield Strength Not specified >=585 MPa (0.2 % proof stress)
Elongation Not specified >=15%
Typical Applications
ASTM A276/A276M S42010
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can ASTM A276/A276M S42010 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
ASTM A276/A276M S42010 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S42010
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S42010 and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 7) 12Cr12MoVH specifies V which is not specified for ASTM A276/A276M S42010.
Can ASTM A276/A276M S42010 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
ASTM A276/A276M S42010 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.