ASTM A276/A276M S44002 vs EN 10088-1 X55CrMo14

Close Alternative — 72.5% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S44002 (ASTM A276/A276M:2017) and EN 10088-1 X55CrMo14 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S44002 is defined under ASTM International, originating from United States, while EN 10088-1 X55CrMo14 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S44002 vs EN 10088-1 X55CrMo14 is a 72.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 72.5%.

Frequently Compared With ASTM A276/A276M S44002:
GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
72.5%
MECHANICAL MATCH
No shared data
OVERALL
72.5%
Specifications
Property ASTM A276/A276M S44002 EN 10088-1 X55CrMo14
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.60-0.75 0.48-0.60
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 16.0-18.0 13.0-15.0
Mo (%) <=0.75 0.50-0.80
V (%) Not specified <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S44002 EN 10088-1 X55CrMo14
Hardness <=269 HB Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S44002
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X55CrMo14
Not documented
Key Differences
Can ASTM A276/A276M S44002 Be Substituted With EN 10088-1 X55CrMo14?
ASTM A276/A276M S44002 and EN 10088-1 X55CrMo14 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M S44002
0 active listings and RFQs →
EN 10088-1 X55CrMo14
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S44002 and EN 10088-1 X55CrMo14?
EN 10088-1 X55CrMo14 specifies V which is not specified for ASTM A276/A276M S44002.
Can ASTM A276/A276M S44002 be substituted with EN 10088-1 X55CrMo14?
ASTM A276/A276M S44002 and EN 10088-1 X55CrMo14 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.