ASTM A276/A276M S44003 vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S44003 (ASTM A276/A276M:2017) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S44003 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware. ASTM A276/A276M S44003 is defined under ASTM International, originating from United States, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S44003 vs EN 10088-1 1.4301 is a 56.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S44003:
EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
56.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A276/A276M S44003 EN 10088-1 1.4301
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.75-0.95 ≤0.07
Mn (%) <=1.00 ≤2.00
P (%) <=0.040 ≤0.045
S (%) <=0.030 ≤0.030
Si (%) <=1.00 ≤1.00
Cr (%) 16.0-18.0 17.5–19.5
Mo (%) <=0.75 Not specified
Ni (%) Not specified 8.0–10.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S44003 EN 10088-1 1.4301
Hardness <=269 HB ≤215 HB
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥210 MPa
Elongation Not specified ≥45%
Typical Applications
ASTM A276/A276M S44003
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
Can ASTM A276/A276M S44003 Be Substituted With EN 10088-1 1.4301?
ASTM A276/A276M S44003 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S44003
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
ASTM A276/A276M S44003
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S44003 and EN 10088-1 1.4301?
ASTM A276/A276M S44003 specifies Mo which is not specified for EN 10088-1 1.4301. EN 10088-1 1.4301 specifies Ni which is not specified for ASTM A276/A276M S44003.
Can ASTM A276/A276M S44003 be substituted with EN 10088-1 1.4301?
ASTM A276/A276M S44003 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.