ASTM A387/A387M Grade 91 vs EN 10028-2 12CrMoV12-10

Minimal Match — 51.1% match based on chemical composition and mechanical property overlap.

ASTM A387/A387M Grade 91 (ASTM A387/A387M:2011) and EN 10028-2 12CrMoV12-10 (EN 10028-2:2017) are both steel grades. Both fall under the Alloy Steel category. ASTM A387/A387M Grade 91 is typically used for welded boilers and pressure vessels for elevated temperature service, while EN 10028-2 12CrMoV12-10 is commonly used for flat products for pressure purposes. ASTM A387/A387M Grade 91 is defined under ASTM International, originating from United States, while EN 10028-2 12CrMoV12-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A387/A387M Grade 91 vs EN 10028-2 12CrMoV12-10 is a 46.3% match. As per mechanical properties, the match is 60.7%. Combined, this makes them a minimal match overall at 51.1%.

Frequently Compared With ASTM A387/A387M Grade 91:
IS 1570 (Part 4) 10Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
46.3%
MECHANICAL MATCH
60.7%
OVERALL
51.1%
Specifications
Property ASTM A387/A387M Grade 91 EN 10028-2 12CrMoV12-10
Standard ASTM A387/A387M:2011 EN 10028-2:2017
Category Alloy Steel Alloy Steel
C (%) 0.08-0.12 0.10-0.15
Mn (%) 0.30-0.60 0.30-0.60
P (%) <=0.020 <=0.015
S (%) <=0.010 <=0.005
Si (%) 0.20-0.50 <=0.15
Cr (%) 8.00-9.50 2.75-3.25
Mo (%) 0.85-1.05 0.90-1.10
Ni (%) <=0.40 <=0.25
V (%) 0.18-0.25 0.20-0.30
Nb (%) 0.06-0.10 <=0.07
N (%) 0.030-0.070 <=0.012
Al (%) <=0.02 Not specified
Ti (%) <=0.01 <=0.03
Zr (%) <=0.01 Not specified
Cu (%) Not specified <=0.25
B (%) Not specified <=0.003
Ca (%) Not specified <=0.015
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A387/A387M Grade 91 EN 10028-2 12CrMoV12-10
Tensile Strength 585-760 MPa 600-780 MPa
Yield Strength >=415 MPa >=455 MPa
Elongation >=18% >=18%
Condition Class 2 plates, no thickness ranges printed; elongation in 50 mm gauge length Usual delivery condition normalized and tempered (+NT), nominal thickness up to 60 mm; transverse direction, Yield Strength is ReH, Elongation is A
Typical Applications
ASTM A387/A387M Grade 91
Welded boilers and pressure vessels for elevated temperature service
EN 10028-2 12CrMoV12-10
Flat products for pressure purposes
Key Differences
Can ASTM A387/A387M Grade 91 Be Substituted With EN 10028-2 12CrMoV12-10?
ASTM A387/A387M Grade 91 and EN 10028-2 12CrMoV12-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A387/A387M Grade 91
0 active listings and RFQs →
EN 10028-2 12CrMoV12-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A387/A387M Grade 91 and EN 10028-2 12CrMoV12-10?
ASTM A387/A387M Grade 91 specifies Al, Zr which are not specified for EN 10028-2 12CrMoV12-10. EN 10028-2 12CrMoV12-10 specifies Cu, B, Ca which are not specified for ASTM A387/A387M Grade 91.
Can ASTM A387/A387M Grade 91 be substituted with EN 10028-2 12CrMoV12-10?
ASTM A387/A387M Grade 91 and EN 10028-2 12CrMoV12-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.