ASTM A537/A537M Class 1 vs BS 970 (Part 3) 045M10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A537/A537M Class 1 (ASTM A537/A537M:2013) and BS 970 (Part 3) 045M10 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. ASTM A537/A537M Class 1 is typically used for fusion welded pressure vessels and structures, while BS 970 (Part 3) 045M10 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (table 14). ASTM A537/A537M Class 1 is defined under ASTM International, originating from United States, while BS 970 (Part 3) 045M10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, ASTM A537/A537M Class 1 vs BS 970 (Part 3) 045M10 is a 63.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A537/A537M Class 1:
BS 970 (Part 3) 045A10 BS 970 (Part 1) 060A45 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A40 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
63.5%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A537/A537M Class 1 BS 970 (Part 3) 045M10
Standard ASTM A537/A537M:2013 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) <=0.24 0.07-0.13
Mn (%) 0.70-1.35 0.30-0.60
P (%) <=0.025 <=0.05
S (%) <=0.025 <=0.05
Si (%) 0.15-0.50 0.10-0.40
Cu (%) <=0.35 Not specified
Ni (%) <=0.25 Not specified
Cr (%) <=0.25 Not specified
Mo (%) <=0.08 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A537/A537M Class 1 BS 970 (Part 3) 045M10
Tensile Strength 485-620 MPa Not specified
Yield Strength >=345 MPa Not specified
Elongation >=22% Not specified
Condition Normalized, thickness 65 mm and under; elongation in 50 mm gauge length Not specified
Typical Applications
ASTM A537/A537M Class 1
Fusion welded pressure vessels and structures
BS 970 (Part 3) 045M10
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (Table 14)
Key Differences
Can ASTM A537/A537M Class 1 Be Substituted With BS 970 (Part 3) 045M10?
ASTM A537/A537M Class 1 and BS 970 (Part 3) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A537/A537M Class 1
0 active listings and RFQs →
BS 970 (Part 3) 045M10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A537/A537M Class 1 and BS 970 (Part 3) 045M10?
ASTM A537/A537M Class 1 specifies Cu, Ni, Cr, Mo which are not specified for BS 970 (Part 3) 045M10.
Can ASTM A537/A537M Class 1 be substituted with BS 970 (Part 3) 045M10?
ASTM A537/A537M Class 1 and BS 970 (Part 3) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.