ASTM A572/A572M Grade 60 vs AS/NZS Grade 500

Strong Match — 95.6% match based on chemical composition and mechanical property overlap.

ASTM A572/A572M Grade 60 (ASTM A572/A572M:2018) and AS/NZS Grade 500 (AS/NZS 3597:2008) are both steel grades. Both fall under the Structural Steel category. ASTM A572/A572M Grade 60 is typically used for riveted or bolted bridge construction, or riveted, bolted or welded construction in other applications, while AS/NZS Grade 500 is commonly used for heavy mining equipment, bulldozer blades, wear-resistant structural applications, large crane booms, offshore jackets.. ASTM A572/A572M Grade 60 is defined under ASTM International, originating from United States, while AS/NZS Grade 500 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, ASTM A572/A572M Grade 60 vs AS/NZS Grade 500 is a 95.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.6%.

Frequently Compared With ASTM A572/A572M Grade 60:
AS/NZS 3679.1 300 CSA G40.21 300W CSA G40.21 260W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 80 ASTM A283C
Other Structural Steel Grades to Compare With ASTM A572/A572M Grade 60:
GOST 19281 09G2S CSA G40.21 400A ASTM A1008 SS Grade 50
Match Breakdown
CHEMISTRY MATCH
95.6%
MECHANICAL MATCH
No shared data
OVERALL
95.6%
Specifications
Property ASTM A572/A572M Grade 60 AS/NZS Grade 500
Standard ASTM A572/A572M:2018 AS/NZS 3597:2008
Category Structural Steel Structural Steel
C (%) <=0.26 max 0.2
Mn (%) <=1.35 max 1.6
P (%) <=0.030 max 0.03
S (%) <=0.030 max 0.03
Si (%) <=0.40 max 0.55
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A572/A572M Grade 60 AS/NZS Grade 500
Tensile Strength >=520 MPa Not specified
Yield Strength >=415 MPa Not specified
Elongation >=16% Not specified
Condition Tension test per Table 4; one set of minimum values for all product thicknesses; Elongation is in 200 mm gauge length, 50 mm values in the tensile block Not specified
Typical Applications
ASTM A572/A572M Grade 60
Riveted or bolted bridge construction, or riveted, bolted or welded construction in other applications
AS/NZS Grade 500
Heavy mining equipment, bulldozer blades, wear-resistant structural applications, large crane booms, offshore jackets.
Can ASTM A572/A572M Grade 60 Be Substituted With AS/NZS Grade 500?
ASTM A572/A572M Grade 60 and AS/NZS Grade 500 overlap closely enough on chemistry and mechanical properties that AS/NZS Grade 500 is often considered as a substitute for ASTM A572/A572M Grade 60 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
ASTM A572/A572M Grade 60
No active listings currently.
AS/NZS Grade 500
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3100–3600 mm (122.05–141.73 in)
On M-EX Right Now
ASTM A572/A572M Grade 60
0 active listings and RFQs →
AS/NZS Grade 500
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A572/A572M Grade 60 and AS/NZS Grade 500?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A572/A572M Grade 60 be substituted with AS/NZS Grade 500?
ASTM A572/A572M Grade 60 and AS/NZS Grade 500 overlap closely enough on chemistry and mechanical properties that AS/NZS Grade 500 is often considered as a substitute for ASTM A572/A572M Grade 60 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.