Close Alternative — 75.2% match
based on chemical composition and mechanical property overlap.
ASTM A572/A572M Grade 42 (ASTM A572/A572M:2021) and IS 2062 E410A (IS 2062:2011) are both steel grades.
Both fall under the Structural Steel category.
ASTM A572/A572M Grade 42 is typically used for riveted, bolted or welded structures, while IS 2062 E410A is commonly used for high strength structural applications.
ASTM A572/A572M Grade 42 is defined under ASTM International, originating from United States, while IS 2062 E410A is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A572/A572M Grade 42 vs IS 2062 E410A is a 96.2% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a close alternative overall at 75.2%.
Frequently Compared With ASTM A572/A572M Grade 42:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Tension test per Table 4; one set of minimum values for all product thicknesses; Elongation is in 200 mm gauge length, 50 mm values in the tensile block
Not specified
Impact
Not specified
not required
Typical Applications
ASTM A572/A572M Grade 42
Riveted, bolted or welded structures
IS 2062 E410A
High strength structural applications
Key Differences
IS 2062 E410A specifies CEV which is not specified for ASTM A572/A572M Grade 42.
Can ASTM A572/A572M Grade 42 Be Substituted With IS 2062 E410A?
ASTM A572/A572M Grade 42 and IS 2062 E410A are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A572/A572M Grade 42 and IS 2062 E410A?
IS 2062 E410A specifies CEV which is not specified for ASTM A572/A572M Grade 42.
Can ASTM A572/A572M Grade 42 be substituted with IS 2062 E410A?
ASTM A572/A572M Grade 42 and IS 2062 E410A are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.