ASTM A572 Grade 50 vs ASTM A283C

Related Material — 66.1% match based on chemical composition and mechanical property overlap.

ASTM A572 Grade 50 (ASTM A572) and ASTM A283C (ASTM A283) are both steel grades. Both fall under the Structural Steel category. ASTM A572 Grade 50 is typically used for high-strength low-alloy structural steel; buildings, bridges, transmission towers, construction equipment, general structural fabrication, while ASTM A283C is commonly used for used for structural fabrication, storage tanks, buildings, bridges, machinery bases, and welded structures.. ASTM A572 Grade 50 is defined under ASTM International, originating from United States, while ASTM A283C is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A572 Grade 50 vs ASTM A283C is a 93% match. As per mechanical properties, the match is 12.3%. Combined, this makes them a related material overall at 66.1%.

Frequently Compared With ASTM A572 Grade 50:
ASTM A572 Gr.65 GOST 19281 09G2S CSA G40.21 260W CSA G40.21 300W AS/NZS 3679.1 300 AS/NZS 3679.1 350 CSA G40.21 480W CSA G40.21 400W CSA G40.21 400A CSA G40.21 350W ASTM A1008 SS Grade 80 ASTM A1008 SS Grade 50
Match Breakdown
CHEMISTRY MATCH
93%
MECHANICAL MATCH
12.3%
OVERALL
66.1%
Specifications
Property ASTM A572 Grade 50 ASTM A283C
Standard ASTM A572 ASTM A283
Category Structural Steel Structural Steel
C (%) <=0.23 0.24 max
Mn (%) <=1.35 0.90 max
Si (%) <=0.40 0.40 max
P (%) <=0.040 0.035 max
S (%) <=0.050 0.040 max
Nb (%) <=0.05 Not specified
V (%) <=0.15 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A572 Grade 50 ASTM A283C
Tensile Strength 450 MPa min 380-515 MPa
Yield Strength 345 MPa min 205 MPa min
Elongation 18% min 23-27%
Hardness 137-187 HB 120-170 HB
Typical Applications
ASTM A572 Grade 50
High-strength low-alloy structural steel; buildings, bridges, transmission towers, construction equipment, general structural fabrication
ASTM A283C
Used for structural fabrication, storage tanks, buildings, bridges, machinery bases, and welded structures.
Key Differences
Can ASTM A572 Grade 50 Be Substituted With ASTM A283C?
ASTM A572 Grade 50 and ASTM A283C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A572 Grade 50
Plate → (4 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2800–4600 mm (110.24–181.1 in)
ASTM A283C
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3700 mm (114.17–145.67 in)
On M-EX Right Now
ASTM A572 Grade 50
4 active listings and RFQs →
ASTM A283C
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A572 Grade 50 and ASTM A283C?
ASTM A572 Grade 50 specifies Nb, V which are not specified for ASTM A283C.
Can ASTM A572 Grade 50 be substituted with ASTM A283C?
ASTM A572 Grade 50 and ASTM A283C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.