Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
Si
Cr
V
W
Mo
2.00-2.85
0.20-0.80
<=0.030
<=0.030
0.10-0.70
5.00-5.75
3.90-5.15
0.50-1.50
0.90-1.40
Mechanical Properties
Hardness
<=269 HB
Condition
Annealed (maximum Brinell hardness)
More data from ASTM A681:2008
From the standard
Maximum hardness in delivery condition2 conditions
Condition
Maximum hardness (HB)
Annealed
269
Cold drawn
285
Maximum Brinell hardness (BHN).
Source: A681:2008, Table 2
Heat treatment and response to hardeninghardening test conditions
Preheat temperature
1500 deg F (816 deg C)
Austenitizing, salt bath
1750 deg F (954 deg C)
Austenitizing, controlled atmosphere furnace
1775 deg F (968 deg C)
Austenitizing time
5 to 15 min
Quench medium
Air
Tempering temperature
400 deg F (204 deg C)
Minimum hardness after treatment
63 HRC
Austenitizing temperatures are stipulated for the response to hardening test only.
Source: A681:2008, Table 3