Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
Si
Cr
W
0.35-0.45
0.20-0.60
<=0.030
<=0.030
0.80-1.25
4.75-5.50
4.00-5.25
Mechanical Properties
Hardness
<=235 HB
Condition
Annealed (maximum Brinell hardness)
More data from ASTM A681:2008
From the standard
Maximum hardness in delivery condition2 conditions
Condition
Maximum hardness (HB)
Annealed
235
Cold drawn
262
Maximum Brinell hardness (BHN).
Source: A681:2008, Table 2
Heat treatment and response to hardeninghardening test conditions
Preheat temperature
1450 deg F (788 deg C)
Austenitizing, salt bath
1900 deg F (1038 deg C)
Austenitizing, controlled atmosphere furnace
1925 deg F (1052 deg C)
Austenitizing time
5 to 15 min
Quench medium
Air
Tempering temperature
1025 deg F (552 deg C)
Minimum hardness after treatment
55 HRC
Austenitizing temperatures are stipulated for the response to hardening test only.
Source: A681:2008, Table 3
Active ASTM A681:2008 H14 Listings on M-EX (For Sale)