ASTM A681 H19 vs GB/T 1299 3Cr2W8V

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A681 H19 (ASTM A681:2008) and GB/T 1299 3Cr2W8V (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 H19 is typically used for tools, dies and fixtures (clause 1.2), while GB/T 1299 3Cr2W8V is commonly used for used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.. ASTM A681 H19 is defined under ASTM International, originating from United States, while GB/T 1299 3Cr2W8V is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, ASTM A681 H19 vs GB/T 1299 3Cr2W8V is a 56.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A681 H19:
IS 1570 (Part 6) 103T3 GOST 5950 4H5MFS EN ISO 4957 1.2316 DIN EN ISO 4957 1.2344 EN ISO 683-17 100Cr6 IS 1570 (Part 6) 133T3 GB/T 1299 4Cr5MoSiV DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 118T3 GOST 5950 3H2W8F GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS1
Match Breakdown
CHEMISTRY MATCH
56.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A681 H19 GB/T 1299 3Cr2W8V
Standard ASTM A681:2008 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) 0.32-0.45 0.30-0.40
Mn (%) 0.20-0.50 0.20-0.50
P (%) <=0.030 0.030 max
S (%) <=0.030 0.030 max
Si (%) 0.15-0.50 0.20-0.40
Cr (%) 4.00-4.75 2.20-2.70
V (%) 1.75-2.20 0.20-0.50
W (%) 3.75-4.50 7.50-9.00
Mo (%) 0.30-0.55 Not specified
Co (%) 4.00-4.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 H19 GB/T 1299 3Cr2W8V
Hardness <=241 HB 48-54 HRC
Condition Annealed (maximum Brinell hardness) Not specified
Tensile Strength Not specified 1180-1380 MPa
Yield Strength Not specified 980-1180 MPa
Elongation Not specified 10-14%
Typical Applications
ASTM A681 H19
Tools, dies and fixtures (clause 1.2)
GB/T 1299 3Cr2W8V
Used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.
Key Differences
Can ASTM A681 H19 Be Substituted With GB/T 1299 3Cr2W8V?
ASTM A681 H19 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A681 H19
No active listings currently.
GB/T 1299 3Cr2W8V
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–2900 mm (110.24–114.17 in)
On M-EX Right Now
ASTM A681 H19
0 active listings and RFQs →
GB/T 1299 3Cr2W8V
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 H19 and GB/T 1299 3Cr2W8V?
ASTM A681 H19 specifies Mo, Co which are not specified for GB/T 1299 3Cr2W8V.
Can ASTM A681 H19 be substituted with GB/T 1299 3Cr2W8V?
ASTM A681 H19 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.