ASTM A681 H22 vs IS 1570 (Part 6) T105W6CrV2

Related Material — 66.6% match based on chemical composition and mechanical property overlap.

ASTM A681 H22 (ASTM A681:2008) and IS 1570 (Part 6) T105W6CrV2 (IS 1570 (Part 6):1996) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 H22 is defined under ASTM International, originating from United States, while IS 1570 (Part 6) T105W6CrV2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A681 H22 vs IS 1570 (Part 6) T105W6CrV2 is a 66.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 66.6%.

Frequently Compared With ASTM A681 H22:
DIN EN ISO 4957 1.2344 IS 1570 (Part 6) 103T3 GB/T 1299 3Cr2W8V IS 1570 (Part 6) 118T3 GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS GOST 5950 4H5MFS1 EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 GOST 5950 3H2W8F GB/T 1299 4Cr5MoSiV EN ISO 683-17 100Cr6
Match Breakdown
CHEMISTRY MATCH
66.6%
MECHANICAL MATCH
No shared data
OVERALL
66.6%
Specifications
Property ASTM A681 H22 IS 1570 (Part 6) T105W6CrV2
Standard ASTM A681:2008 IS 1570 (Part 6):1996
Category Tool & Die Steels Tool & Die Steels
C (%) 0.30-0.40 0.90-1.20
Mn (%) 0.15-0.40 <=0.40
P (%) <=0.030 <=0.035
S (%) <=0.030 <=0.035
Si (%) 0.15-0.40 0.10-0.35
Cr (%) 1.75-3.75 0.40-0.80
V (%) 0.25-0.50 0.20-0.30
W (%) 10.00-11.75 1.25-1.75
Mo (%) Not specified <=0.25 (optional)
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 H22 IS 1570 (Part 6) T105W6CrV2
Hardness <=235 HB Not specified
Condition Annealed (maximum Brinell hardness) Not specified
Typical Applications
ASTM A681 H22
Tools, dies and fixtures (clause 1.2)
IS 1570 (Part 6) T105W6CrV2
Not documented
Key Differences
Can ASTM A681 H22 Be Substituted With IS 1570 (Part 6) T105W6CrV2?
ASTM A681 H22 and IS 1570 (Part 6) T105W6CrV2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A681 H22
0 active listings and RFQs →
IS 1570 (Part 6) T105W6CrV2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 H22 and IS 1570 (Part 6) T105W6CrV2?
IS 1570 (Part 6) T105W6CrV2 specifies Mo which is not specified for ASTM A681 H22.
Can ASTM A681 H22 be substituted with IS 1570 (Part 6) T105W6CrV2?
ASTM A681 H22 and IS 1570 (Part 6) T105W6CrV2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.