ASTM A681 L3 vs EN ISO 683-17 100Cr6

Minimal Match — 53.9% match based on chemical composition and mechanical property overlap.

ASTM A681 L3 (ASTM A681:2008) and EN ISO 683-17 100Cr6 (EN ISO 683-17:2014) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 L3 is typically used for tools, dies and fixtures (clause 1.2), while EN ISO 683-17 100Cr6 is commonly used for rolling element bearings, precision components, cold work tooling. ASTM A681 L3 is defined under ASTM International, originating from United States, while EN ISO 683-17 100Cr6 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A681 L3 vs EN ISO 683-17 100Cr6 is a 80.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 53.9%.

Frequently Compared With ASTM A681 L3:
IS 1570 (Part 6) 103T3 GB/T 1299 3Cr2W8V GOST 5950 4H5MFS EN ISO 4957 1.2316 DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 118T3 GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1 IS 1570 (Part 6) 133T3 GOST 5950 3H2W8F GOST 5950 4H5MFS1
Match Breakdown
CHEMISTRY MATCH
80.9%
MECHANICAL MATCH
0%
OVERALL
53.9%
Specifications
Property ASTM A681 L3 EN ISO 683-17 100Cr6
Standard ASTM A681:2008 EN ISO 683-17:2014
Category Tool & Die Steels Tool & Die Steels
C (%) 0.95-1.10 0.93–1.05
Mn (%) 0.25-0.80 0.25–0.45
P (%) <=0.030 ≤0.025
S (%) <=0.030 ≤0.025
Si (%) 0.10-0.50 0.15–0.35
Cr (%) 1.30-1.70 1.35–1.65
V (%) 0.10-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 L3 EN ISO 683-17 100Cr6
Hardness <=201 HB Not specified
Condition Annealed (maximum Brinell hardness) Not specified
Tensile Strength Not specified ≥620 MPa (annealed)
Hardness HRC Not specified 60–66 (hardened)
Hardness HB Not specified 179–217 (annealed)
Typical Applications
ASTM A681 L3
Tools, dies and fixtures (clause 1.2)
EN ISO 683-17 100Cr6
Rolling element bearings, precision components, cold work tooling
Key Differences
Can ASTM A681 L3 Be Substituted With EN ISO 683-17 100Cr6?
ASTM A681 L3 and EN ISO 683-17 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A681 L3
No active listings currently.
EN ISO 683-17 100Cr6
Round Bar → (18 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3000–6500 mm (118.11–255.91 in)
On M-EX Right Now
ASTM A681 L3
0 active listings and RFQs →
EN ISO 683-17 100Cr6
18 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 L3 and EN ISO 683-17 100Cr6?
ASTM A681 L3 specifies V which is not specified for EN ISO 683-17 100Cr6.
Can ASTM A681 L3 be substituted with EN ISO 683-17 100Cr6?
ASTM A681 L3 and EN ISO 683-17 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.