ASTM A959 201L vs ASTM A240/A240M S20103

Strong Match — 98.6% match based on chemical composition and mechanical property overlap.

ASTM A959 201L (ASTM A959:2011) and ASTM A240/A240M S20103 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 201L is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S20103 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 201L is defined under ASTM International, originating from United States, while ASTM A240/A240M S20103 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 201L vs ASTM A240/A240M S20103 is a 98.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.6%.

Frequently Compared With ASTM A959 201L:
ASTM A959 .- ASTM A959 201LN EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
No shared data
OVERALL
98.6%
Specifications
Property ASTM A959 201L ASTM A240/A240M S20103
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.03 <=0.03
Cr (%) 16.0-18.0 16.0-18.0
Mn (%) 5.5-7.5 5.50-7.50
N (%) <=0.25 <=0.25
Ni (%) 3.5-5.5 3.5-5.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 201L ASTM A240/A240M S20103
Tensile Strength Not specified >=655 MPa
Yield Strength Not specified >=260 MPa
Elongation Not specified >=40%
Hardness Not specified <=217 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 201L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S20103
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 201L Be Substituted With ASTM A240/A240M S20103?
ASTM A959 201L and ASTM A240/A240M S20103 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S20103 is often considered as a substitute for ASTM A959 201L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 201L
0 active listings and RFQs →
ASTM A240/A240M S20103
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 201L and ASTM A240/A240M S20103?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 201L be substituted with ASTM A240/A240M S20103?
ASTM A959 201L and ASTM A240/A240M S20103 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S20103 is often considered as a substitute for ASTM A959 201L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.