ASTM A959 2304 vs EN 10088-2 X2CrNiN23-4

Strong Match — 93.1% match based on chemical composition and mechanical property overlap.

ASTM A959 2304 (ASTM A959:2011) and EN 10088-2 X2CrNiN23-4 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 2304 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-2 X2CrNiN23-4 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. ASTM A959 2304 is defined under ASTM International, originating from United States, while EN 10088-2 X2CrNiN23-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 2304 vs EN 10088-2 X2CrNiN23-4 is a 93.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.1%.

Frequently Compared With ASTM A959 2304:
ASTM A959 2205 EN 10088-1 1.4845 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
93.1%
MECHANICAL MATCH
No shared data
OVERALL
93.1%
Specifications
Property ASTM A959 2304 EN 10088-2 X2CrNiN23-4
Standard ASTM A959:2011 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 21.5-24.5 22.0-24.5
Cu (%) 0.05-0.60 0.10-0.60
Mn (%) <=2.50 <=2.00
Mo (%) 0.05-0.60 0.10-0.60
N (%) 0.05-0.20 0.05-0.20
Ni (%) 3.0-5.5 3.5-5.5
P (%) <=0.040 <=0.035
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 2304 EN 10088-2 X2CrNiN23-4
Tensile Strength Not specified 650-850 MPa
Yield Strength Not specified >=450 MPa
Elongation Not specified >=20%
Condition Not specified Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Typical Applications
ASTM A959 2304
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-2 X2CrNiN23-4
General purposes, hot or cold rolled sheet/plate and strip
Can ASTM A959 2304 Be Substituted With EN 10088-2 X2CrNiN23-4?
ASTM A959 2304 and EN 10088-2 X2CrNiN23-4 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrNiN23-4 is often considered as a substitute for ASTM A959 2304 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 2304
0 active listings and RFQs →
EN 10088-2 X2CrNiN23-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 2304 and EN 10088-2 X2CrNiN23-4?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 2304 be substituted with EN 10088-2 X2CrNiN23-4?
ASTM A959 2304 and EN 10088-2 X2CrNiN23-4 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrNiN23-4 is often considered as a substitute for ASTM A959 2304 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.