ASTM A959 255 vs JIS G4305 SUS329J3L

Close Alternative — 78.4% match based on chemical composition and mechanical property overlap.

ASTM A959 255 (ASTM A959:2011) and JIS G4305 SUS329J3L (JIS G4305:2012) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 255 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4305 SUS329J3L is commonly used for cold-rolled stainless steel plates, sheet and strip. ASTM A959 255 is defined under ASTM International, originating from United States, while JIS G4305 SUS329J3L is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 255 vs JIS G4305 SUS329J3L is a 78.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 78.4%.

Frequently Compared With ASTM A959 255:
ASTM A959 2507 ASTM A959 2205 ASTM A959 26-3-3 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
78.4%
MECHANICAL MATCH
No shared data
OVERALL
78.4%
Specifications
Property ASTM A959 255 JIS G4305 SUS329J3L
Standard ASTM A959:2011 JIS G4305:2012
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Cr (%) 24.0-27.0 21.00-24.00
Cu (%) 1.50-2.50 Not specified
Mn (%) <=1.50 <=2.00
Mo (%) 2.9-3.9 2.50-3.50
N (%) 0.10-0.25 0.08-0.20
Ni (%) 4.5-6.5 4.50-6.50
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 255 JIS G4305 SUS329J3L
Tensile Strength Not specified >=620 MPa
Yield Strength Not specified >=450 MPa
Elongation Not specified >=18%
Hardness Not specified <=302 HB
Condition Not specified Solution heat treated plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 255
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4305 SUS329J3L
Cold-rolled stainless steel plates, sheet and strip
Key Differences
Can ASTM A959 255 Be Substituted With JIS G4305 SUS329J3L?
ASTM A959 255 and JIS G4305 SUS329J3L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 255
0 active listings and RFQs →
JIS G4305 SUS329J3L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 255 and JIS G4305 SUS329J3L?
ASTM A959 255 specifies Cu which is not specified for JIS G4305 SUS329J3L.
Can ASTM A959 255 be substituted with JIS G4305 SUS329J3L?
ASTM A959 255 and JIS G4305 SUS329J3L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.