ASTM A959 302 vs ASTM A240/A240M S30200

Strong Match — 98.6% match based on chemical composition and mechanical property overlap.

ASTM A959 302 (ASTM A959:2011) and ASTM A240/A240M S30200 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 302 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S30200 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 302 is defined under ASTM International, originating from United States, while ASTM A240/A240M S30200 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 302 vs ASTM A240/A240M S30200 is a 98.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.6%.

Frequently Compared With ASTM A959 302:
EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 202 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
No shared data
OVERALL
98.6%
Specifications
Property ASTM A959 302 ASTM A240/A240M S30200
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.15
Cr (%) 17.0-19.0 17.0-19.0
Mn (%) <=2.00 <=2.00
N (%) <=0.10 <=0.10
Ni (%) 8.0-10.0 8.0-10.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 302 ASTM A240/A240M S30200
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=40%
Hardness Not specified <=201 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 302
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S30200
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 302 Be Substituted With ASTM A240/A240M S30200?
ASTM A959 302 and ASTM A240/A240M S30200 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S30200 is often considered as a substitute for ASTM A959 302 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 302
0 active listings and RFQs →
ASTM A240/A240M S30200
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 302 and ASTM A240/A240M S30200?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 302 be substituted with ASTM A240/A240M S30200?
ASTM A959 302 and ASTM A240/A240M S30200 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S30200 is often considered as a substitute for ASTM A959 302 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.