ASTM A959 304L vs IS 1570 (Part 5) X02Cr19Ni10

Strong Match — 98.3% match based on chemical composition and mechanical property overlap.

ASTM A959 304L (ASTM A959:2011) and IS 1570 (Part 5) X02Cr19Ni10 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 304L is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 304L vs IS 1570 (Part 5) X02Cr19Ni10 is a 98.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.3%.

Frequently Compared With ASTM A959 304L:
EN 10088-1 1.4301 GOST 5632 08X18H10 EN 10088-1 1.4845 ASTM A959 201L ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
98.3%
MECHANICAL MATCH
No shared data
OVERALL
98.3%
Specifications
Property ASTM A959 304L IS 1570 (Part 5) X02Cr19Ni10
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 17.5-19.5 17.5-20.0
Mn (%) <=2.00 <=2.0
Ni (%) 8.0-12.0 8.0-12.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 304L IS 1570 (Part 5) X02Cr19Ni10
Tensile Strength Not specified >=485 MPa
Yield Strength Not specified >=170 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=183 HB; <=88 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A959 304L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 5) X02Cr19Ni10
Not documented
Can ASTM A959 304L Be Substituted With IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 304L and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for ASTM A959 304L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 304L
0 active listings and RFQs →
IS 1570 (Part 5) X02Cr19Ni10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 304L and IS 1570 (Part 5) X02Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 304L be substituted with IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 304L and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for ASTM A959 304L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.