ASTM A959 304LHN vs ASTM A240/A240M S30453

Strong Match — 91% match based on chemical composition and mechanical property overlap.

ASTM A959 304LHN (ASTM A959:2011) and ASTM A240/A240M S30453 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 304LHN is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S30453 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 304LHN is defined under ASTM International, originating from United States, while ASTM A240/A240M S30453 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 304LHN vs ASTM A240/A240M S30453 is a 91% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91%.

Frequently Compared With ASTM A959 304LHN:
ASTM A959 201LN EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
91%
MECHANICAL MATCH
No shared data
OVERALL
91%
Specifications
Property ASTM A959 304LHN ASTM A240/A240M S30453
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.03 <=0.030
Cr (%) 18.0-20.0 18.0-20.0
Mn (%) <=2.00 <=2.00
N (%) 0.16-0.30 0.10-0.16
Ni (%) 8.0-11.0 8.0-12.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 304LHN ASTM A240/A240M S30453
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=40%
Hardness Not specified <=217 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 304LHN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S30453
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 304LHN Be Substituted With ASTM A240/A240M S30453?
ASTM A959 304LHN and ASTM A240/A240M S30453 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S30453 is often considered as a substitute for ASTM A959 304LHN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 304LHN
0 active listings and RFQs →
ASTM A240/A240M S30453
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 304LHN and ASTM A240/A240M S30453?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 304LHN be substituted with ASTM A240/A240M S30453?
ASTM A959 304LHN and ASTM A240/A240M S30453 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S30453 is often considered as a substitute for ASTM A959 304LHN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.