ASTM A959 304LHN vs IS 1570 (Part 5) X02Cr19Ni10

Strong Match — 90.7% match based on chemical composition and mechanical property overlap.

ASTM A959 304LHN (ASTM A959:2011) and IS 1570 (Part 5) X02Cr19Ni10 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 304LHN is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 304LHN vs IS 1570 (Part 5) X02Cr19Ni10 is a 90.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.7%.

Frequently Compared With ASTM A959 304LHN:
ASTM A959 201LN EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
90.7%
MECHANICAL MATCH
No shared data
OVERALL
90.7%
Specifications
Property ASTM A959 304LHN IS 1570 (Part 5) X02Cr19Ni10
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.03 <=0.030
Cr (%) 18.0-20.0 17.5-20.0
Mn (%) <=2.00 <=2.0
N (%) 0.16-0.30 Not specified
Ni (%) 8.0-11.0 8.0-12.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 304LHN IS 1570 (Part 5) X02Cr19Ni10
Tensile Strength Not specified >=485 MPa
Yield Strength Not specified >=170 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=183 HB; <=88 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A959 304LHN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 5) X02Cr19Ni10
Not documented
Key Differences
Can ASTM A959 304LHN Be Substituted With IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 304LHN and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for ASTM A959 304LHN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 304LHN
0 active listings and RFQs →
IS 1570 (Part 5) X02Cr19Ni10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 304LHN and IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 304LHN specifies N which is not specified for IS 1570 (Part 5) X02Cr19Ni10.
Can ASTM A959 304LHN be substituted with IS 1570 (Part 5) X02Cr19Ni10?
ASTM A959 304LHN and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for ASTM A959 304LHN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.