ASTM A959 310MoLN vs IS 1570 (Part 7) 12Cr13H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A959 310MoLN (ASTM A959:2011) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 310MoLN is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. ASTM A959 310MoLN is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 310MoLN vs IS 1570 (Part 7) 12Cr13H is a 52.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A959 310MoLN:
ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
52.9%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A959 310MoLN IS 1570 (Part 7) 12Cr13H
Standard ASTM A959:2011 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.09-0.15
Cr (%) 24.0-26.0 11.5-14.00
Mn (%) <=2.00 <=1.00
Mo (%) 2.00-3.00 Not specified
N (%) 0.10-0.16 Not specified
Ni (%) 21.0-23.0 <=1.00
P (%) <=0.030 <=0.040
S (%) <=0.015 <=0.030
Si (%) <=0.40 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 310MoLN IS 1570 (Part 7) 12Cr13H
Tensile Strength Not specified 470-670 MPa
Yield Strength Not specified >=265 MPa (0.2 % proof stress)
Elongation Not specified >=20%
Condition Not specified Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Typical Applications
ASTM A959 310MoLN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can ASTM A959 310MoLN Be Substituted With IS 1570 (Part 7) 12Cr13H?
ASTM A959 310MoLN and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 310MoLN
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr13H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 310MoLN and IS 1570 (Part 7) 12Cr13H?
ASTM A959 310MoLN specifies Mo, N which are not specified for IS 1570 (Part 7) 12Cr13H.
Can ASTM A959 310MoLN be substituted with IS 1570 (Part 7) 12Cr13H?
ASTM A959 310MoLN and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.