Strong Match — 93.1% match based on chemical composition and mechanical property overlap.

ASTM A959 317LMN (ASTM A959:2011) and ASTM A240/A240M S31725 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 317LMN is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S31725 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 317LMN is defined under ASTM International, originating from United States, while ASTM A240/A240M S31725 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 317LMN vs ASTM A240/A240M S31725 is a 93.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.1%.

Frequently Compared With ASTM A959 317LMN:
GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4401 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
93.1%
MECHANICAL MATCH
No shared data
OVERALL
93.1%
Specifications
Property ASTM A959 317LMN ASTM A240/A240M S31725
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 17.0-20.0 18.0-20.0
Mn (%) <=2.00 <=2.00
Mo (%) 4.0-5.0 4.0-5.0
N (%) 0.10-0.20 <=0.20
Ni (%) 13.5-17.5 13.5-17.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 317LMN ASTM A240/A240M S31725
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=40%
Hardness Not specified <=217 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 317LMN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S31725
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 317LMN Be Substituted With ASTM A240/A240M S31725?
ASTM A959 317LMN and ASTM A240/A240M S31725 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S31725 is often considered as a substitute for ASTM A959 317LMN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 317LMN
0 active listings and RFQs →
ASTM A240/A240M S31725
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 317LMN and ASTM A240/A240M S31725?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 317LMN be substituted with ASTM A240/A240M S31725?
ASTM A959 317LMN and ASTM A240/A240M S31725 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S31725 is often considered as a substitute for ASTM A959 317LMN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.