ASTM A959 348H vs IS 1570 (Part 7) 7Cr18Ni11NbH

Strong Match — 92.4% match based on chemical composition and mechanical property overlap.

ASTM A959 348H (ASTM A959:2011) and IS 1570 (Part 7) 7Cr18Ni11NbH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 348H is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 1570 (Part 7) 7Cr18Ni11NbH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. ASTM A959 348H is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 7Cr18Ni11NbH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 348H vs IS 1570 (Part 7) 7Cr18Ni11NbH is a 92.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.4%.

Frequently Compared With ASTM A959 348H:
GOST 5632 06Kh23N28 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
92.4%
MECHANICAL MATCH
No shared data
OVERALL
92.4%
Specifications
Property ASTM A959 348H IS 1570 (Part 7) 7Cr18Ni11NbH
Standard ASTM A959:2011 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.04-0.10 0.04-0.10
Co (%) <=0.20 Not specified
Cr (%) 17.0-19.0 17.00-19.00
Mn (%) <=2.00 <=2.00
Ni (%) 9.0-12.0 9.00-13.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
Ta (%) <=0.10 Not specified
Nb+Ta (%) Not specified >=10xC, <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 348H IS 1570 (Part 7) 7Cr18Ni11NbH
Tensile Strength Not specified 510-710 MPa
Yield Strength Not specified >=205 MPa (0.2 % proof stress)
Elongation Not specified >=30%
Condition Not specified Pipes, bars, forgings, plates, Q, thickness - (first row of Table 3)
Typical Applications
ASTM A959 348H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 7) 7Cr18Ni11NbH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can ASTM A959 348H Be Substituted With IS 1570 (Part 7) 7Cr18Ni11NbH?
ASTM A959 348H and IS 1570 (Part 7) 7Cr18Ni11NbH overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 7) 7Cr18Ni11NbH is often considered as a substitute for ASTM A959 348H in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 348H
0 active listings and RFQs →
IS 1570 (Part 7) 7Cr18Ni11NbH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 348H and IS 1570 (Part 7) 7Cr18Ni11NbH?
ASTM A959 348H specifies Co, Ta which are not specified for IS 1570 (Part 7) 7Cr18Ni11NbH. IS 1570 (Part 7) 7Cr18Ni11NbH specifies Nb+Ta which is not specified for ASTM A959 348H.
Can ASTM A959 348H be substituted with IS 1570 (Part 7) 7Cr18Ni11NbH?
ASTM A959 348H and IS 1570 (Part 7) 7Cr18Ni11NbH overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 7) 7Cr18Ni11NbH is often considered as a substitute for ASTM A959 348H in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.