Post Stock Login Register

ASTM A959 409Cb vs ASTM A240/A240M S41008

Strong Match — 87.7% match based on chemical composition and mechanical property overlap.

ASTM A959 409Cb (ASTM A959:2011) and ASTM A240/A240M S41008 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 409Cb is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S41008 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 409Cb is defined under ASTM International, originating from United States, while ASTM A240/A240M S41008 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 409Cb vs ASTM A240/A240M S41008 is a 87.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.7%.

Frequently Compared With ASTM A959 409Cb:
EN 10088-1 1.4401 ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
87.7%
MECHANICAL MATCH
No shared data
OVERALL
87.7%
Specifications
Property ASTM A959 409Cb ASTM A240/A240M S41008
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.08
Cr (%) 10.5-11.7 11.5-13.5
Mn (%) <=1.00 <=1.00
Ni (%) <=0.50 <=0.60
P (%) <=0.045 <=0.040
S (%) <=0.040 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 409Cb ASTM A240/A240M S41008
Tensile Strength Not specified >=415 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=22%
Hardness Not specified <=183 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 409Cb
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S41008
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 409Cb Be Substituted With ASTM A240/A240M S41008?
ASTM A959 409Cb and ASTM A240/A240M S41008 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S41008 is often considered as a substitute for ASTM A959 409Cb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 409Cb
0 active listings and RFQs →
ASTM A240/A240M S41008
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 409Cb and ASTM A240/A240M S41008?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 409Cb be substituted with ASTM A240/A240M S41008?
ASTM A959 409Cb and ASTM A240/A240M S41008 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S41008 is often considered as a substitute for ASTM A959 409Cb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.