ASTM A959 410Cb vs ASTM A276/A276M S41040

Strong Match — 92.4% match based on chemical composition and mechanical property overlap.

ASTM A959 410Cb (ASTM A959:2011) and ASTM A276/A276M S41040 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 410Cb is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A276/A276M S41040 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). ASTM A959 410Cb is defined under ASTM International, originating from United States, while ASTM A276/A276M S41040 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 410Cb vs ASTM A276/A276M S41040 is a 92.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.4%.

Frequently Compared With ASTM A959 410Cb:
EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
92.4%
MECHANICAL MATCH
No shared data
OVERALL
92.4%
Specifications
Property ASTM A959 410Cb ASTM A276/A276M S41040
Standard ASTM A959:2011 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.18 <=0.18
Cb (%) 0.05-0.30 Not specified
Cr (%) 11.5-13.0 11.0-13.0
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Nb (%) Not specified 0.05-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 410Cb ASTM A276/A276M S41040
Tensile Strength Not specified >=480 MPa
Yield Strength Not specified >=275 MPa
Elongation Not specified >=13%
Hardness Not specified <=235 HB
Condition Not specified Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
ASTM A959 410Cb
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A276/A276M S41040
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can ASTM A959 410Cb Be Substituted With ASTM A276/A276M S41040?
ASTM A959 410Cb and ASTM A276/A276M S41040 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S41040 is often considered as a substitute for ASTM A959 410Cb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 410Cb
0 active listings and RFQs →
ASTM A276/A276M S41040
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 410Cb and ASTM A276/A276M S41040?
ASTM A959 410Cb specifies Cb which is not specified for ASTM A276/A276M S41040. ASTM A276/A276M S41040 specifies Nb which is not specified for ASTM A959 410Cb.
Can ASTM A959 410Cb be substituted with ASTM A276/A276M S41040?
ASTM A959 410Cb and ASTM A276/A276M S41040 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S41040 is often considered as a substitute for ASTM A959 410Cb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.