Strong Match — 92.5% match based on chemical composition and mechanical property overlap.

ASTM A959 410Cb (ASTM A959:2011) and IS 11169 (Part 2) X12Cr12 (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 410Cb is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X12Cr12 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1). ASTM A959 410Cb is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X12Cr12 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 410Cb vs IS 11169 (Part 2) X12Cr12 is a 92.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.5%.

Frequently Compared With ASTM A959 410Cb:
EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
92.5%
MECHANICAL MATCH
No shared data
OVERALL
92.5%
Specifications
Property ASTM A959 410Cb IS 11169 (Part 2) X12Cr12
Standard ASTM A959:2011 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) <=0.18 0.08-0.15
Cb (%) 0.05-0.30 Not specified
Cr (%) 11.5-13.0 11.5-13.5
Mn (%) <=1.00 <=1.0
P (%) <=0.040 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 410Cb IS 11169 (Part 2) X12Cr12
Yield Strength (0.2% proof) Not specified >=450 MPa
Tensile Strength Not specified 600-750 MPa
Elongation Not specified >=18%
Impact (U-notch 5 mm) Not specified >=50 J
Condition Not specified Quenched and tempered reference test piece (Table 6 treatment)
Typical Applications
ASTM A959 410Cb
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X12Cr12
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Key Differences
Can ASTM A959 410Cb Be Substituted With IS 11169 (Part 2) X12Cr12?
ASTM A959 410Cb and IS 11169 (Part 2) X12Cr12 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X12Cr12 is often considered as a substitute for ASTM A959 410Cb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 410Cb
0 active listings and RFQs →
IS 11169 (Part 2) X12Cr12
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 410Cb and IS 11169 (Part 2) X12Cr12?
ASTM A959 410Cb specifies Cb which is not specified for IS 11169 (Part 2) X12Cr12.
Can ASTM A959 410Cb be substituted with IS 11169 (Part 2) X12Cr12?
ASTM A959 410Cb and IS 11169 (Part 2) X12Cr12 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X12Cr12 is often considered as a substitute for ASTM A959 410Cb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.