ASTM A959 430Ti vs ASTM A240/A240M S43000

Strong Match — 95% match based on chemical composition and mechanical property overlap.

ASTM A959 430Ti (ASTM A959:2011) and ASTM A240/A240M S43000 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 430Ti is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S43000 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 430Ti is defined under ASTM International, originating from United States, while ASTM A240/A240M S43000 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 430Ti vs ASTM A240/A240M S43000 is a 95% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95%.

Frequently Compared With ASTM A959 430Ti:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
95%
MECHANICAL MATCH
No shared data
OVERALL
95%
Specifications
Property ASTM A959 430Ti ASTM A240/A240M S43000
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.10 <=0.12
Cr (%) 16.0-19.5 16.0-18.0
Mn (%) <=1.00 <=1.00
Ni (%) <=0.75 <=0.75
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 430Ti ASTM A240/A240M S43000
Tensile Strength Not specified >=450 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=22%
Hardness Not specified <=183 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 430Ti
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S43000
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 430Ti Be Substituted With ASTM A240/A240M S43000?
ASTM A959 430Ti and ASTM A240/A240M S43000 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S43000 is often considered as a substitute for ASTM A959 430Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 430Ti
0 active listings and RFQs →
ASTM A240/A240M S43000
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 430Ti and ASTM A240/A240M S43000?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 430Ti be substituted with ASTM A240/A240M S43000?
ASTM A959 430Ti and ASTM A240/A240M S43000 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S43000 is often considered as a substitute for ASTM A959 430Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.