Strong Match — 95% match
based on chemical composition and mechanical property overlap.
ASTM A959 430Ti (ASTM A959:2011) and IS 5522 X07Cr17 (IS 5522:2014) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 430Ti is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 5522 X07Cr17 is commonly used for utensils.
ASTM A959 430Ti is defined under ASTM International, originating from United States, while IS 5522 X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 430Ti vs IS 5522 X07Cr17 is a 95% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 95%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 430Ti
IS 5522 X07Cr17
Tensile Strength
Not specified
>=450 MPa
Yield Strength
Not specified
>=205 MPa
Elongation
Not specified
>=20%
Hardness
Not specified
<=183 HB
Condition
Not specified
Annealed/softened
Typical Applications
ASTM A959 430Ti
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 5522 X07Cr17
Utensils
Can ASTM A959 430Ti Be Substituted With IS 5522 X07Cr17?
ASTM A959 430Ti and IS 5522 X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 5522 X07Cr17 is often considered as a substitute for ASTM A959 430Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between ASTM A959 430Ti and IS 5522 X07Cr17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 430Ti be substituted with IS 5522 X07Cr17?
ASTM A959 430Ti and IS 5522 X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 5522 X07Cr17 is often considered as a substitute for ASTM A959 430Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.