ASTM A959 615 vs BS 970 (Part 3) 416S37

Related Material — 66.2% match based on chemical composition and mechanical property overlap.

ASTM A959 615 (ASTM A959:2011) and BS 970 (Part 3) 416S37 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 615 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while BS 970 (Part 3) 416S37 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (table 17). ASTM A959 615 is defined under ASTM International, originating from United States, while BS 970 (Part 3) 416S37 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, ASTM A959 615 vs BS 970 (Part 3) 416S37 is a 66.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 66.2%.

Frequently Compared With ASTM A959 615:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
66.2%
MECHANICAL MATCH
No shared data
OVERALL
66.2%
Specifications
Property ASTM A959 615 BS 970 (Part 3) 416S37
Standard ASTM A959:2011 BS 970 (Part 3):1991
Category Stainless Steel Stainless Steel
C (%) 0.15-0.20 0.20-0.28
Cr (%) 12.0-14.0 12.0-14.0
Mn (%) <=0.50 <=1.5
Mo (%) <=0.50 <=0.60
Ni (%) 1.80-2.20 <=1.00
P (%) <=0.040 <=0.060
S (%) <=0.030 0.15-0.35
Si (%) <=0.50 <=1.0
W (%) 2.5-3.5 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 615
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
BS 970 (Part 3) 416S37
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (Table 17)
Key Differences
Can ASTM A959 615 Be Substituted With BS 970 (Part 3) 416S37?
ASTM A959 615 and BS 970 (Part 3) 416S37 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 615
0 active listings and RFQs →
BS 970 (Part 3) 416S37
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 615 and BS 970 (Part 3) 416S37?
ASTM A959 615 specifies W which is not specified for BS 970 (Part 3) 416S37.
Can ASTM A959 615 be substituted with BS 970 (Part 3) 416S37?
ASTM A959 615 and BS 970 (Part 3) 416S37 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.