ASTM A959 619 vs EN 10083-1 2C30

Related Material — 65% match based on chemical composition and mechanical property overlap.

ASTM A959 619 (ASTM A959:2011) and EN 10083-1 2C30 (EN 10083-1:1991) are both steel grades. ASTM A959 619 is classified under Stainless Steel, while EN 10083-1 2C30 is classified under Carbon Steel — a different category, which is worth noting alongside the chemistry match below. ASTM A959 619 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10083-1 2C30 is commonly used for quenched and tempered machine parts; non alloy steels also normalized (clause 1). ASTM A959 619 is defined under ASTM International, originating from United States, while EN 10083-1 2C30 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 619 vs EN 10083-1 2C30 is a 65.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With ASTM A959 619:
IS 1570 (Part 7) 20Cr12MoNiVH IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
65.5%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property ASTM A959 619 EN 10083-1 2C30
Standard ASTM A959:2011 EN 10083-1:1991
Category Stainless Steel Carbon Steel
C (%) 0.27-0.32 0.27-0.34
Cr (%) 11.0-12.0 <=0.40
Mn (%) 0.95-1.35 0.50-0.80
Mo (%) 2.50-3.00 <=0.10
Ni (%) <=0.50 <=0.40
P (%) <=0.025 <=0.035
S (%) <=0.025 <=0.035
Si (%) <=0.50 <=0.40
V (%) 0.20-0.30 Not specified
Cr+Mo+Ni (%) Not specified <=0.63
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 619 EN 10083-1 2C30
Condition Not specified Quenched and tempered, ruling section d <= 16 mm
Elongation Not specified 18% min
Tensile Strength Not specified 600 to 750 MPa
Yield Strength Not specified 400 MPa min
Typical Applications
ASTM A959 619
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10083-1 2C30
Quenched and tempered machine parts; non alloy steels also normalized (clause 1)
Key Differences
Can ASTM A959 619 Be Substituted With EN 10083-1 2C30?
ASTM A959 619 and EN 10083-1 2C30 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 619
0 active listings and RFQs →
EN 10083-1 2C30
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 619 and EN 10083-1 2C30?
Different category: ASTM A959 619 is Stainless Steel, EN 10083-1 2C30 is Carbon Steel. ASTM A959 619 specifies V which is not specified for EN 10083-1 2C30. EN 10083-1 2C30 specifies Cr+Mo+Ni which is not specified for ASTM A959 619.
Can ASTM A959 619 be substituted with EN 10083-1 2C30?
ASTM A959 619 and EN 10083-1 2C30 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.