Strong Match — 87.5% match
based on chemical composition and mechanical property overlap.
ASTM A959 631 (ASTM A959:2011) and IS 6911 X10Cr17Ni7 (IS 6911:1992) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 631 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 6911 X10Cr17Ni7 is commonly used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1).
ASTM A959 631 is defined under ASTM International, originating from United States, while IS 6911 X10Cr17Ni7 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 631 vs IS 6911 X10Cr17Ni7 is a 87.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 87.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 631
IS 6911 X10Cr17Ni7
Bend Test (180 deg)
Not specified
Not required
Elongation (50 mm, annealed)
Not specified
>=40%
Hardness (annealed, max)
Not specified
212 HBS
Tensile Strength (annealed)
Not specified
>=590 MPa
Yield Strength (0.2% proof, annealed)
Not specified
>=220 MPa
Typical Applications
ASTM A959 631
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 6911 X10Cr17Ni7
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
Key Differences
ASTM A959 631 specifies Al which is not specified for IS 6911 X10Cr17Ni7.
Can ASTM A959 631 Be Substituted With IS 6911 X10Cr17Ni7?
ASTM A959 631 and IS 6911 X10Cr17Ni7 overlap closely enough on chemistry and mechanical properties that IS 6911 X10Cr17Ni7 is often considered as a substitute for ASTM A959 631 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between ASTM A959 631 and IS 6911 X10Cr17Ni7?
ASTM A959 631 specifies Al which is not specified for IS 6911 X10Cr17Ni7.
Can ASTM A959 631 be substituted with IS 6911 X10Cr17Ni7?
ASTM A959 631 and IS 6911 X10Cr17Ni7 overlap closely enough on chemistry and mechanical properties that IS 6911 X10Cr17Ni7 is often considered as a substitute for ASTM A959 631 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.