ASTM A959 651 vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A959 651 (ASTM A959:2011) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 651 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware. ASTM A959 651 is defined under ASTM International, originating from United States, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 651 vs EN 10088-1 1.4301 is a 50.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A959 651:
GOST 5632 06Kh23N28 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
50.8%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A959 651 EN 10088-1 1.4301
Standard ASTM A959:2011 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.28-0.35 ≤0.07
Cb (%) 0.25-0.60 Not specified
Cr (%) 18.0-21.0 17.5–19.5
Cu (%) <=0.50 Not specified
Mn (%) 0.75-1.50 ≤2.00
Mo (%) 1.00-1.75 Not specified
Ni (%) 8.0-11.0 8.0–10.5
P (%) <=0.040 ≤0.045
S (%) <=0.030 ≤0.030
Si (%) 0.30-0.80 ≤1.00
Ti (%) 0.10-0.35 Not specified
W (%) 1.00-1.75 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 651 EN 10088-1 1.4301
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥210 MPa
Elongation Not specified ≥45%
Hardness Not specified ≤215 HB
Typical Applications
ASTM A959 651
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
Can ASTM A959 651 Be Substituted With EN 10088-1 1.4301?
ASTM A959 651 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 651
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
ASTM A959 651
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 651 and EN 10088-1 1.4301?
ASTM A959 651 specifies Cb, Cu, Mo, Ti which are not specified for EN 10088-1 1.4301.
Can ASTM A959 651 be substituted with EN 10088-1 1.4301?
ASTM A959 651 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.