ASTM A959 N08020 vs IS 1570 (Part 5) X04Cr17Ni12Mo2Ti

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 N08020 (ASTM A959:2011) and IS 1570 (Part 5) X04Cr17Ni12Mo2Ti (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 N08020 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 N08020 vs IS 1570 (Part 5) X04Cr17Ni12Mo2Ti is a 73.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 N08020:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
73.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 N08020 IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.07 <=0.08
Cr (%) 19.0-21.0 16.0-18.0
Cu (%) 3.0-4.0 Not specified
Mn (%) <=2.00 <=2.0
Mo (%) 2.00-3.00 2.0-3.0
Ni (%) 32.0-38.0 10.0-14.0
P (%) <=0.045 <=0.045
S (%) <=0.035 <=0.030
Si (%) <=1.00 <=1.0
Ti (%) Not specified <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 N08020 IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=217 HB; <=95 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A959 N08020
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
Not documented
Key Differences
Can ASTM A959 N08020 Be Substituted With IS 1570 (Part 5) X04Cr17Ni12Mo2Ti?
ASTM A959 N08020 and IS 1570 (Part 5) X04Cr17Ni12Mo2Ti share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 N08020
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 N08020 and IS 1570 (Part 5) X04Cr17Ni12Mo2Ti?
ASTM A959 N08020 specifies Cu which is not specified for IS 1570 (Part 5) X04Cr17Ni12Mo2Ti. IS 1570 (Part 5) X04Cr17Ni12Mo2Ti specifies Ti which is not specified for ASTM A959 N08020.
Can ASTM A959 N08020 be substituted with IS 1570 (Part 5) X04Cr17Ni12Mo2Ti?
ASTM A959 N08020 and IS 1570 (Part 5) X04Cr17Ni12Mo2Ti share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.