Strong Match — 100% match
based on chemical composition and mechanical property overlap.
ASTM A959 N08367 (ASTM A959:2011) and ASTM A276/A276M N08367 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 N08367 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A276/A276M N08367 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
ASTM A959 N08367 is defined under ASTM International, originating from United States, while ASTM A276/A276M N08367 is defined under ASTM International, originating from United States.
As per chemical composition, ASTM A959 N08367 vs ASTM A276/A276M N08367 is a 100% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 100%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 N08367
ASTM A276/A276M N08367
Tensile Strength
Not specified
>=655 MPa
Yield Strength
Not specified
>=310 MPa
Elongation
Not specified
>=30%
Condition
Not specified
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
ASTM A959 N08367
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A276/A276M N08367
Stainless steel bars and shapes (hot-finished or cold-finished)
Can ASTM A959 N08367 Be Substituted With ASTM A276/A276M N08367?
ASTM A959 N08367 and ASTM A276/A276M N08367 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M N08367 is often considered as a substitute for ASTM A959 N08367 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between ASTM A959 N08367 and ASTM A276/A276M N08367?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 N08367 be substituted with ASTM A276/A276M N08367?
ASTM A959 N08367 and ASTM A276/A276M N08367 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M N08367 is often considered as a substitute for ASTM A959 N08367 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.