ASTM A959 N08367 vs ASTM A959 N08926

Close Alternative — 79% match based on chemical composition and mechanical property overlap.

ASTM A959 N08367 (ASTM A959:2011) and ASTM A959 N08926 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 N08367 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 N08926 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 N08367 is defined under ASTM International, originating from United States, while ASTM A959 N08926 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 N08367 vs ASTM A959 N08926 is a 79% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 79%.

Frequently Compared With ASTM A959 N08367:
ASTM A959 2304 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
79%
MECHANICAL MATCH
No shared data
OVERALL
79%
Specifications
Property ASTM A959 N08367 ASTM A959 N08926
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.020
Cr (%) 20.0-22.0 19.0-21.0
Cu (%) <=0.75 0.50-1.50
Mn (%) <=2.00 <=2.00
Mo (%) 6.0-7.0 6.0-7.0
N (%) 0.18-0.25 0.15-0.25
Ni (%) 23.5-25.5 24.0-26.0
P (%) <=0.040 <=0.030
S (%) <=0.030 <=0.010
Si (%) <=1.00 <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 N08367
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 N08926
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A959 N08367 Be Substituted With ASTM A959 N08926?
ASTM A959 N08367 and ASTM A959 N08926 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 N08367
0 active listings and RFQs →
ASTM A959 N08926
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 N08367 and ASTM A959 N08926?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 N08367 be substituted with ASTM A959 N08926?
ASTM A959 N08367 and ASTM A959 N08926 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.