Close Alternative — 81.2% match
based on chemical composition and mechanical property overlap.
ASTM A959 N08367 (ASTM A959:2011) and IS 6603 X01Ni25Cr20Mo7CuN (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 N08367 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 6603 X01Ni25Cr20Mo7CuN is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
ASTM A959 N08367 is defined under ASTM International, originating from United States, while IS 6603 X01Ni25Cr20Mo7CuN is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 N08367 vs IS 6603 X01Ni25Cr20Mo7CuN is a 81.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 81.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 N08367
IS 6603 X01Ni25Cr20Mo7CuN
Tensile Strength
Not specified
650-850 MPa
Yield Strength
Not specified
>=300 MPa
Elongation
Not specified
>=40%
Condition
Not specified
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
ASTM A959 N08367
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 6603 X01Ni25Cr20Mo7CuN
General purposes, semi-finished products, bars, wire rods and bright bars
Can ASTM A959 N08367 Be Substituted With IS 6603 X01Ni25Cr20Mo7CuN?
ASTM A959 N08367 and IS 6603 X01Ni25Cr20Mo7CuN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A959 N08367 and IS 6603 X01Ni25Cr20Mo7CuN?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 N08367 be substituted with IS 6603 X01Ni25Cr20Mo7CuN?
ASTM A959 N08367 and IS 6603 X01Ni25Cr20Mo7CuN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.