ASTM A959 S20162 vs JIS G4304 SUS315J2

Related Material — 65.5% match based on chemical composition and mechanical property overlap.

ASTM A959 S20162 (ASTM A959:2011) and JIS G4304 SUS315J2 (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S20162 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS315J2 is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 S20162 is defined under ASTM International, originating from United States, while JIS G4304 SUS315J2 is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 S20162 vs JIS G4304 SUS315J2 is a 65.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.5%.

Frequently Compared With ASTM A959 S20162:
EN 10088-1 1.4006 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
65.5%
MECHANICAL MATCH
No shared data
OVERALL
65.5%
Specifications
Property ASTM A959 S20162 JIS G4304 SUS315J2
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.08
Cr (%) 16.5-21.0 17.00-20.50
Mn (%) 4.0-8.0 <=2.00
Mo (%) 0.50-2.50 0.50-1.50
N (%) 0.05-0.25 Not specified
Ni (%) 6.0-10.0 11.00-14.00
P (%) <=0.040 <=0.045
S (%) <=0.040 <=0.030
Si (%) 2.5-4.5 2.50-4.00
Cu (%) Not specified 0.50-3.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S20162 JIS G4304 SUS315J2
Tensile Strength Not specified >=520 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=40%
Hardness Not specified <=187 HB
Condition Not specified Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 S20162
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS315J2
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 S20162 Be Substituted With JIS G4304 SUS315J2?
ASTM A959 S20162 and JIS G4304 SUS315J2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 S20162
0 active listings and RFQs →
JIS G4304 SUS315J2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S20162 and JIS G4304 SUS315J2?
ASTM A959 S20162 specifies N which is not specified for JIS G4304 SUS315J2. JIS G4304 SUS315J2 specifies Cu which is not specified for ASTM A959 S20162.
Can ASTM A959 S20162 be substituted with JIS G4304 SUS315J2?
ASTM A959 S20162 and JIS G4304 SUS315J2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.