Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
ASTM A959 S28200 (ASTM A959:2011) and IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 S28200 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X04Cr17Mo1 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, table 13).
ASTM A959 S28200 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 S28200 vs IS 11169 (Part 2) X04Cr17Mo1 is a 74.4% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 S28200
IS 11169 (Part 2) X04Cr17Mo1
Reduction of Area, soft annealed (+A)
Not specified
>=60% (over 5 to 25 mm)
Tensile Strength, soft annealed (+A)
Not specified
<=600 MPa (over 5 to 25 mm)
Typical Applications
ASTM A959 S28200
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
Key Differences
ASTM A959 S28200 specifies Cu, N which are not specified for IS 11169 (Part 2) X04Cr17Mo1.
Can ASTM A959 S28200 Be Substituted With IS 11169 (Part 2) X04Cr17Mo1?
ASTM A959 S28200 and IS 11169 (Part 2) X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A959 S28200 and IS 11169 (Part 2) X04Cr17Mo1?
ASTM A959 S28200 specifies Cu, N which are not specified for IS 11169 (Part 2) X04Cr17Mo1.
Can ASTM A959 S28200 be substituted with IS 11169 (Part 2) X04Cr17Mo1?
ASTM A959 S28200 and IS 11169 (Part 2) X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.