ASTM A959 S28200 vs IS 6603 X04Cr17Mo1

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 S28200 (ASTM A959:2011) and IS 6603 X04Cr17Mo1 (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S28200 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 6603 X04Cr17Mo1 is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars. ASTM A959 S28200 is defined under ASTM International, originating from United States, while IS 6603 X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S28200 vs IS 6603 X04Cr17Mo1 is a 72.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 S28200:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
72.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 S28200 IS 6603 X04Cr17Mo1
Standard ASTM A959:2011 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.08
Cr (%) 17.0-19.0 16.0-18.0
Cu (%) 0.75-1.25 Not specified
Mn (%) 17.0-19.0 <=1.00
Mo (%) 0.75-1.25 0.90-1.40
N (%) 0.40-0.60 Not specified
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S28200 IS 6603 X04Cr17Mo1
Tensile Strength Not specified >=440 MPa
Condition Not specified Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, size range to be agreed; Tensile Strength is a minimum as printed
Typical Applications
ASTM A959 S28200
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 6603 X04Cr17Mo1
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
Can ASTM A959 S28200 Be Substituted With IS 6603 X04Cr17Mo1?
ASTM A959 S28200 and IS 6603 X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 S28200
0 active listings and RFQs →
IS 6603 X04Cr17Mo1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S28200 and IS 6603 X04Cr17Mo1?
ASTM A959 S28200 specifies Cu, N which are not specified for IS 6603 X04Cr17Mo1.
Can ASTM A959 S28200 be substituted with IS 6603 X04Cr17Mo1?
ASTM A959 S28200 and IS 6603 X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.