ASTM A959 S30432 vs IS 5522 X07Cr18Ni9

Close Alternative — 72.7% match based on chemical composition and mechanical property overlap.

ASTM A959 S30432 (ASTM A959:2011) and IS 5522 X07Cr18Ni9 (IS 5522:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S30432 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 5522 X07Cr18Ni9 is commonly used for utensils. ASTM A959 S30432 is defined under ASTM International, originating from United States, while IS 5522 X07Cr18Ni9 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S30432 vs IS 5522 X07Cr18Ni9 is a 72.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 72.7%.

Frequently Compared With ASTM A959 S30432:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
72.7%
MECHANICAL MATCH
No shared data
OVERALL
72.7%
Specifications
Property ASTM A959 S30432 IS 5522 X07Cr18Ni9
Standard ASTM A959:2011 IS 5522:2014
Category Stainless Steel Stainless Steel
Al (%) 0.003-0.030 Not specified
B (%) 0.001-0.010 Not specified
C (%) 0.07-0.13 <=0.12
Cb (%) 0.20-0.60 Not specified
Cr (%) 17.0-19.0 17.0-19.0
Cu (%) 2.5-3.5 Not specified
Mn (%) <=0.50 <=2.00
N (%) 0.05-0.12 <=0.10
Ni (%) 7.5-10.5 8.0-10.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=0.30 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S30432 IS 5522 X07Cr18Ni9
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=40%
Hardness Not specified <=201 HB
Condition Not specified Annealed/softened
Typical Applications
ASTM A959 S30432
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 5522 X07Cr18Ni9
Utensils
Key Differences
Can ASTM A959 S30432 Be Substituted With IS 5522 X07Cr18Ni9?
ASTM A959 S30432 and IS 5522 X07Cr18Ni9 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S30432
0 active listings and RFQs →
IS 5522 X07Cr18Ni9
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S30432 and IS 5522 X07Cr18Ni9?
ASTM A959 S30432 specifies Al, B, Cb, Cu which are not specified for IS 5522 X07Cr18Ni9.
Can ASTM A959 S30432 be substituted with IS 5522 X07Cr18Ni9?
ASTM A959 S30432 and IS 5522 X07Cr18Ni9 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.