ASTM A959 S31260 vs ASTM A240/A240M S31260

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A959 S31260 (ASTM A959:2011) and ASTM A240/A240M S31260 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S31260 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S31260 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 S31260 is defined under ASTM International, originating from United States, while ASTM A240/A240M S31260 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S31260 vs ASTM A240/A240M S31260 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A959 S31260:
ASTM A959 2507 ASTM A959 255 GOST 5632 08X18H10 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A959 S31260 ASTM A240/A240M S31260
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.03
Cr (%) 24.0-26.0 24.0-26.0
Cu (%) 0.20-0.80 0.20-0.80
Mn (%) <=1.00 <=1.00
Mo (%) 2.5-3.5 2.5-3.5
N (%) 0.10-0.30 0.10-0.30
Ni (%) 5.5-7.5 5.5-7.5
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Si (%) <=0.75 <=0.75
W (%) 0.10-0.50 0.10-0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S31260 ASTM A240/A240M S31260
Tensile Strength Not specified >=690 MPa
Yield Strength Not specified >=485 MPa
Elongation Not specified >=20%
Hardness Not specified <=290 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 S31260
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S31260
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 S31260 Be Substituted With ASTM A240/A240M S31260?
ASTM A959 S31260 and ASTM A240/A240M S31260 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S31260 is often considered as a substitute for ASTM A959 S31260 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S31260
0 active listings and RFQs →
ASTM A240/A240M S31260
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S31260 and ASTM A240/A240M S31260?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S31260 be substituted with ASTM A240/A240M S31260?
ASTM A959 S31260 and ASTM A240/A240M S31260 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S31260 is often considered as a substitute for ASTM A959 S31260 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.