ASTM A959 S31260 vs JIS G4305 SUS329J4L

Strong Match — 87.2% match based on chemical composition and mechanical property overlap.

ASTM A959 S31260 (ASTM A959:2011) and JIS G4305 SUS329J4L (JIS G4305:2012) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S31260 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4305 SUS329J4L is commonly used for cold-rolled stainless steel plates, sheet and strip. ASTM A959 S31260 is defined under ASTM International, originating from United States, while JIS G4305 SUS329J4L is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 S31260 vs JIS G4305 SUS329J4L is a 87.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.2%.

Frequently Compared With ASTM A959 S31260:
ASTM A959 2507 ASTM A959 255 GOST 5632 08X18H10 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
No shared data
OVERALL
87.2%
Specifications
Property ASTM A959 S31260 JIS G4305 SUS329J4L
Standard ASTM A959:2011 JIS G4305:2012
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 24.0-26.0 24.00-26.00
Cu (%) 0.20-0.80 Not specified
Mn (%) <=1.00 <=1.50
Mo (%) 2.5-3.5 2.50-3.50
N (%) 0.10-0.30 0.08-0.30
Ni (%) 5.5-7.5 5.50-7.50
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=0.75 <=1.00
W (%) 0.10-0.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S31260 JIS G4305 SUS329J4L
Tensile Strength Not specified >=620 MPa
Yield Strength Not specified >=450 MPa
Elongation Not specified >=18%
Hardness Not specified <=302 HB
Condition Not specified Solution heat treated plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 S31260
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4305 SUS329J4L
Cold-rolled stainless steel plates, sheet and strip
Key Differences
Can ASTM A959 S31260 Be Substituted With JIS G4305 SUS329J4L?
ASTM A959 S31260 and JIS G4305 SUS329J4L overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS329J4L is often considered as a substitute for ASTM A959 S31260 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S31260
0 active listings and RFQs →
JIS G4305 SUS329J4L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S31260 and JIS G4305 SUS329J4L?
ASTM A959 S31260 specifies Cu, W which are not specified for JIS G4305 SUS329J4L.
Can ASTM A959 S31260 be substituted with JIS G4305 SUS329J4L?
ASTM A959 S31260 and JIS G4305 SUS329J4L overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS329J4L is often considered as a substitute for ASTM A959 S31260 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.